Melting behavior of fusible materials according to UN/ECE Regulation No. 118, Annex 7

The burning rate of horizontally mounted materials designed to be used in vehicles and buses must be tested with the UN/ECE R118 annex 6 test before they can be approved for use. Measurlabs offers this and the other R118 tests with accreditation. In the test method, the exposed side of the test specimen is burned from underneath and the burning rate is measured and expressed in mm/min.

ISO 5659-2 outlines the procedure for measuring the optical density of smoke produced by a material placed in a closed test cabinet and exposed to thermal radiation. The standard was originally developed for plastics, but it can be applied to a range of other products and materials. In the test, representative specimens of the material are mounted horizontally in a test chamber, and their upper surface is exposed to a specified level of thermal irradiance (usually 25 kW/m2 or 50 kW/m2), with or without a pilot flame. The resulting smoke is collected, and its optical density is measured using a photometric method. Some of the key parameters measured include the maximum specific optical density (Ds,max), the specific optical densities at specified times (Ds(1,5), Ds(4), Ds(10)), and the cumulative specific optical densities during the first 4 minutes of the test (VOF4). A toxicity measurement can also be included to measure toxic gas emissions. Its results are reported as the conventional index of toxicity (CITG). The ISO 5659-2 smoke production test is often required as part of the EN 45545-2 fire safety evaluation of railway materials.

This method is used to determine the gross heat of combustion of solid building products at constant volume in a bomb calorimeter. Results are reported in J/kg. If the product is non-homogeneous, meaning that it consists of multiple materials, each material must be tested separately. The result can be used to classify construction products into classes A1, A1fl, A1L, A2, A2fl, and A2L according to the fire classification standard EN 13501-1.

Fire testing according to EN ISO 9239-1 is used to evaluate the ability of flooring to withstand flames and radiant heat. Flame spread, smoke generation, and the lowest radiant heat to sustain burning are measured. The method is primarily used to classify floor coverings according to the European EN 13501-1 fire classification system. Depending on the results, floorings can be categorized as A2fl, Bfl, Cfl, or Dfl. A smoke production classification of s1 or s2 is also provided. Another use case is assessing the burning behavior of floor composites and interior horizontal surfaces used in rail vehicles according to the EN 45545-2 standard. The testing procedure is the following: 1) The test specimen is placed in a horizontal position below a gas-fired radiant panel inclined at 30°, where it is exposed to a defined heat flux. 2) A pilot flame is applied to the hotter end of the specimen. 3) Following ignition, any flame front that develops is noted, and a record is made of the progression of the flame front horizontally along the length of the specimen, measuring the time it takes for the fire to spread to defined distances. 4) Smoke production is recorded as light transmission in the exhaust stack. One specimen is tested in one direction (e.g. production direction) and another in the direction perpendicular to the first specimen. The test that yields the worst results is repeated twice in that direction.

The ISO 4589-2 oxygen index test is used to evaluate the fire behavior of certain railway materials according to the EN 45545-2 standard. It is required to meet requirements R22, R23, and R24, which apply to products such as insulators, seals, pipes, and hoses. The oxygen index (OI) is the minimum volume-based percentage of oxygen in an oxygen-nitrogen mixture required to support the combustion of the sample under specified conditions. For a material to meet EN 45545-2 requirements, the OI must be at least 28% (hazard classes HL1 and HL2) or at least 32% (HL3). Testing is performed on 20 replicate samples, with the required specimen size depending on the material: 80−150 mm x 10 mm x 4 mm for mould-made materials, such as plastics, 80−150 mm x 10 mm x 10 mm for porous materials, such as foams, 140 mm x 52 mm x d, where d < 10.5 mm, for flexible films, sheets, and fabrics.

Fire classification of construction materials is generally performed by the European classification standard EN 13501-1. The price displayed on this page includes the preparation of the classification report. The tests can be purchased separately. The tests required for EN 13501-1 fire classification include the following: For non-flooring: Class F and E: EN ISO 11925-2, Class D, C, B: EN ISO 11925-2 and EN 13823, Class A2: EN 13823 and EN ISO 1182 or EN ISO 1716, Class A1: EN ISO 1182 and EN ISO 1716. For flooring : Class Ffl and Efl: EN ISO 11925-2, Class Dfl, Cfl, Bfl: EN ISO 11925-2 and EN ISO 9239-1, Class A2fl: EN ISO 9239-1 and EN ISO 1182 or EN ISO 1716, Class A1fl: EN ISO 1182 and EN ISO 1716. For linear pipes: Class FL and EL: EN ISO 11925-2, Class DL, CL, BL: EN ISO 11925-2 and EN 13823, Class A2L: EN 13823 and EN ISO 1182 or EN ISO 1716, Class A1L: EN ISO 1182 and EN ISO 1716. In addition to the main class, the materials are given additional classifications for smoke production (s1, s2, and s3) and burning particles (d0, d1, and d2).

This test measures the ignitability of building materials when exposed to a small flame. The main purpose of the test is to classify building products according to Euroclass B, Bfl, BL, C, Cfl, CL, D, Dfl, DL, E, Efl, or EL as per the European classification standard EN 13501-1. Measurlabs provides individual EN ISO 11925-2 testing as well as other certified tests for EN 13501-1 fire rating classification.

The burning rate of vertically mounted materials designed for vehicles and buses must be tested with the UN/ECE R118 Annex 8 test before approval for use. Measurlabs offers this and other accredited R118 fire tests. Upon meeting the requirements outlined in Annex 8, the requirements for horizontal flame spread (annex 6) are also met. In the test method, the exposed side of the vertically mounted test specimen is burned from underneath and the burning rate is measured in mm/min.

ISO 5660-1 outlines a procedure for using a cone calorimeter to measure the heat release and smoke production rates of materials upon exposure to a predetermined heat flux. Before testing, representative specimens are conditioned at 23±2 ℃ and 50±5% RH until reaching constant mass. They are then wrapped in foil, placed in a sample holder within a retainer frame, and exposed to an irradiance of 50±1 kW/m2 (unless specified otherwise). The results will include the maximum average rate of heat emission (MARHE), which is required information for multiple material types when evaluating their fire safety in railway applications according to EN 45545-2. Other measured parameters include the following: Mass at the start and end of the experiment, Mass loss percentage, Average mass loss rate, Ignition and extinction times, Maximum rate of heat release (RHR), RHR at 180 and 300 seconds after starting the test, Total heat release (THR), Total smoke production per unit area (overall + before and after ignition). We can also offer other reaction-to-fire tests to meet EN 45545-2 requirements, including ISO 5658-2 and ISO 5659-2. Do not hesitate to contact our experts if you need a quote for the full set of tests.

The EN 17084 standard outlines two ways to evaluate the toxicity potential of combustion products that are formed when a material intended for railway applications burns: ISO 5659-2 Smoke chamber test, used to determine the Conventional Index of Toxicity (CITG) of products that cover large surface areas., NF X70-100 Tube furnace test, used to determine the CIT of non-listed products, i.e., small-mass minor components.. We offer both of these tests, along with others described in the EN 45545-2 standard on the fire behavior of railway materials. Please contact our experts for more information and a quote for the full set of tests.